Property Test Method
CERTIFIED PROPERTIES
Thickness (mils nominal) ASTM 5199 10 20 30 40 60
Thickness, min. ASTM D792 .0095" .019" .0285" .038" .057"
Min. Tensile Properties
1. Strength at Break ASTM D882, Min (MD & TD) 24 lbs/in. 48 lbs/in. 73 lbs/in. 97 lbs/in. 137 lbs/in.
2. Elongation at Break (%) ASTM D882 250% 360% 380% 430% 450%
3. Modulus @ 100% Elongation ASTM D882 10 lbs/in. 21 lbs/in. 32 lbs/in. 40 lbs/in. 60 lbs/in.
Tear Strength (min. average lbs) ASTM D 1004 2.5 6 8 10 15
Dimensional Stability ASTM D1204, Max Chg (MD & TD) 4% 4% 3% 3% 3%
Low Temperature Impact ASTM D1790, Pass -10° F -15° F -20° F -20° F -20° F
INDEX PROPERTIES
Specific Gravity ASTM D792, Typical 1.2 1.2 1.2 1.2 1.2
Water Extraction (Max. % wt loss) ASTM D1239 0.15% 0.15% 0.15% 0.20% 0.20%
Average Plasticizer Molecular Weight ASTM D2124 400 400 400 400 400
Volatile Loss (Max % wt loss) ASTM D1203 1.5% 0.9% 0.7% 0.5% 0.5%
Resistance to Soil Burial (%Δ max in original value)
1. Breaking Factor ASTM G160 5% 5% 5% 5% 5%
2. Elongation at Break (%) ASTM G160 20% 20% 20% 20% 20%
3. Modulus (Force) @ 100% Elongation ASTM G160 20% 20% 20% 20% 20%
Hydrostatic Resistance (lbs/sq.in. min) ASTM D751 42 psi 68 psi 100 psi 120 psi 180 psi
SEAM REQUIREMENTS
Factory Seaming Method Dielectric Fusion Weld
Shear Strength (lbs/in min)ASTM D3083 20 lbs/in 38.4 lbs/in 58.4 lbs/in 77.6 lbs/in 116 lbs/in
Peel Adhesion (lbs/in min) ASTM D413 10 lbs/in 12.5 lbs/in 15 lbs/in 15 lbs/in 15 lbs/in
Polyvinyl Chloride (PVC)
Values
SPECIFICATION SHEET
All information, recommendations and suggestions appearing in this literature concerning the use of our products are based upon test and data believed to be reliable; however, it is
the user's responsibility to determine the suitability for their own use of the products described herein. Since the actual use by others is beyond our control, no guarantee or
warranty of any kind, expressed or implied, is made by AccuGeo Liner, Inc. as to the effects of such use or the results to be obtained, nor does AccuGeo Liner, Inc. assume any
liability in connection herewith. Any Statement made herein may not be absolutely complete since additional information may be necessary or desirable when particular or
exceptional conditions or circumstances exist or because of applicable laws or government regulations. Nothing herein contained is to be construed as permission or as a
recommendation to infringe any patent.